Nickel & Nickel Alloys
N10276 • 2.4819
- Application
C276 is a nickel-molybdenum-chromium superalloy with an addition oftungsten designed to have excellent corrosion resistance in a wide range of severe environments. The high chromium, molybdenum and tungsten contents make the alloy especially resistant to pitting and crevice corrosion in reducing environments while chromium conveys resistance to oxidizing media. The low carbon content minimizes carbide precipitation during welding to maintain corrosion resistance in as-welded structures.
Alloy C276 is resistant to the formation of grain boundary precipitates in the weld heat-affected zone, thus making it suitable for most chemical process application in an as welded condition. Alloy C276 is widely used in the most severe environments such as mixed acid chemical processing, pollution control, pulp and paper production, industrial and municipal waste treatment, and recovery of sour oil and gas.
- Typical manufacturing specifications
ASTM B622
Also individual customer specifications.
- Industries predominantly using this grade
Chemical processes, Oil and gas etc.
Technical Data
Chemical composition(% by Weight)
Element | Cr | Mo | Fe | W | C | Si | Co | Mn | V | P | S |
|---|---|---|---|---|---|---|---|---|---|---|---|
Minimum | 14.5 | 15.0 | 4.0 | 3.0 | - | - | - | - | - | - | - |
Maximum | 16.5 | 17.0 | 7.0 | 4.5 | 0.001 | 0.08 | 2.50 | 1.0 | 0.35 | 0.04 | 0.03 |
Aiming | 15.5 | 16.0 | 6.0 | 3.5 | 0.003 | 0.02 | 2.8 | 0.1 | 0.05 | 0.001 | 0.001 |
Mechanical Properties
| Specifications(Tubing, Annealed) | Actual data | |||
|---|---|---|---|---|
Tensile Rm | 100 | ksi (min.) | 108 ~ 130 | ksi (min.) |
Tensile Rm | 690 | MPa (min.) | 750 ~ 900 | MPa (min.) |
Yield (R.p. 0.2%) | 41 | ksi (min.) | 50 ~ 72 | ksi (min.) |
Yield (R.p. 0.2%) | 283 | MPa (min.) | 350 ~ 500 | MPa (min.) |
Elongation | 40 | % (min.) | 50 ~ 60 | % (min.) |